Unlocking the organic residues preserved in the corrosion from the Pewsey Hoard vessels

Scientific Reports volume 12, Article number: 21284 (2022) Cite this article

2238 Accesses

12 Altmetric

Metrics details

The characterization of archaeological metal corrosion has traditionally been limited to the identification of inorganic compounds usually by X-ray diffraction (XRD), thought to result from the interaction between the metal object and the deposition environment. The discovery of a hoard of Late Roman copper-alloy vessels in Wiltshire, UK presented an unique opportunity to adopt a multi-analytical approach to characterize corrosion combining XRD with Fourier-transform infrared (FTIR) and gas chromatography with quadrupole time-of-flight mass spectrometry using a thermal separation probe (GC-QTOF-MS with TSP). This approach revealed organic compounds potentially historical preserved within crystalline inorganic matrices. It has been known for some time that ceramics can harbour organic residues, which provide crucial evidence about the use of these vessels in the past. Our results confirms that similar residues appear to survive in metal corrosion thus extending the potential for identification of biomaterials used in the past.

The identification of substances used in the past enhances our understanding of cultural practices and everyday life in the past1. Although the earliest analyses of visible archaeological residues were undertaken in the early twentieth century2, it was the coupling of chromatography with mass spectrometry 50 years later that enabled the chemical profiling of complex organic residues3,4.

The study of archaeological organic residues is complicated by chemical changes due to the processing of substances (e.g. mixing, cooking) in the past, their degradation during deposition, and contamination5. Notwithstanding these complexities, an increasing number of markers for specific substances are being reported in the literature (e.g.4,6,7,8,9,10,11,12,13,14,15,16,17,18). Currently, organic residues are mostly extracted from porous ceramic sherds4—their porosity believed to confer some protection against degradation and contamination in a way which is yet to be fully understood.

Conservators routinely find macro-organic remains such as fibres, insects, pollen and plant fragments “mineralized” by archaeological copper corrosion products, particularly from metal objects recovered from graves19. In copper alloy objects, preservation of organic residues may include encapsulation by inorganic salts20 aided by copper’s biocidal properties21,22,23,24 and the formation of metal–organic complexes25.

In a pilot study of bronze corrosion, Merriman et al.26 recovered pine resin and oil markers from the corrosion of a patera, a pan-like object found in ritual contexts throughout the Roman empire. The innovation of this study was the targeting of corrosion for organic residue analysis, as opposed to visually distinguishable residues (e.g.21,27,28,29,30). The researchers suggested that the organic compounds recovered had been encapsulated by inorganic compounds (although these were not identified as part of the study) as opposed to being trapped in the sample as metal–organic or organometallic complexes which would be harder to detect.

Indeed, corrosion experiments have demonstrated that copper ions readily react with organic and inorganic ligands in the same medium31 forming copper-organic complexes and characteristic inorganic phases. Moreover, the low solubility of copper-organic complexes in organic solvents32 and/or the presence of copper ions negatively impact the recovery of organic residues by typical gas chromatography with mass spectrometry protocols33. Thus the discovery of the Pewsey Hoard provided a unique opportunity to investigate archaeological corrosion from difference vessels with the same deposition context by incorporating techniques targeting both inorganic and organic compounds.

The Pewsey Hoard is a group of Late Roman copper-alloy vessels found by metal detectorists in 2014 in a field in the Vale of Pewsey, Wiltshire (UK)34. Excavated by the finders themselves, it consists of a large iron-rimmed copper-alloy cauldron (Fig. 1a,b) holding two bowls (Vessels A and C) and another vessel (Vessel B) containing four scale pans carefully packed with plants (Fig. 1c). Subsequent excavation of the area surrounding the findspot by Historic England concluded that the hoard was deposited in a pit, dug in an actively used landscape with no structures or ditches in its immediate vicinity35.

Source: https://finds.org.uk/database/artefacts/record/id/720549.

The Pewsey Hoard (a) graphic representation of the arrangement of the objects (b) the main vessels as delivered to Salisbury Museum (c) plant remains found in Vessel B.

Although several Late Roman hoards containing cauldrons and bowls have been found in Britain, the Pewsey Hoard is unusual because of the inclusion of scale pans and plant packing material. The combination of objects of different functions points to the broad economic value of metal artefacts but the inclusion of the scale pans (possibly pairs given their similar weight and dimension), uncommon in a rural setting, suggests a symbolic intention36. Analysis of the various grassy woodland plant remains found “mineralized” in Vessel B due to a specific microclimate, indicates that the hoard was deposited in an arable field immediately after the cereal harvest, sometime within AD 345–405 period. The discovery, in 2020, of a Late Roman coin hoard containing of 160 silver coins37 scattered in the same field emphasizes the importance of the site within the wider landscape.

The corrosion covering the Pewsey Hoard vessels varied in colour and texture, sometimes within the same vessel (Table 1) suggesting exposure of the metal surface to different environments, prior and/or during deposition. Therefore, the sampling strategy adopted for this study was based on the following considerations:

The closest corrosion layer to the metallic surface would be most likely to contain historic significant residues;

Substances related to vessel use may be present in the interior corrosion but not in the exterior;

The areas to be sampled should be those less likely to have been contaminated due to handling during excavation;

A soil sample from within the hoard would act as blank/control.

To target inorganic and organic phases within the same sample we adopted a multi-analytical approach for the characterization of the Pewsey Hoard corrosion comprised of:

Fourier-transform infrared (FTIR) a popular technique with museum conservators for the identification of organic and inorganic materials;

Powder X-ray diffraction (XRD) a technique used for the identification of crystalline compounds, commonly used for the identification of mineral phases in archaeological metal corrosion;

Gas chromatography with quadrupole time-of-flight mass spectrometry using a thermal separation probe (GC-QTOF-MS with TSP) a relatively recent technique for the study of organic residues trapped in inorganic matrices such as soils38.

The aim of our study was to investigate if organic residues were preserved in association with mineral phases, consider if these residues could be of historical value and evaluate the analytical techniques.

Initially, the cauldron rim corrosion samples were analysed by FTIR in ATR mode but this technique resulted in a spectra with poorly-defined bands and baseline. In an attempt to obtain an improved spectra, the interior corrosion of the vessel was analysed using the KBr method, which is destructive. There wasn't enough exterior sample to analyse by this method.

Diagnostic bands in the FTIR spectra (Fig. 2) of the cauldron rim interior corrosion are: strong bands at 3445 and 3336 cm−1 representing N–H asymmetric and O–H stretching vibrations, a medium broad band centered around 1639 cm−1 encompassing N–H amide and C=C vibrations and a strong peak at 1030 cm−1 characteristic of silicates39. The absence of bands around 2900–2880 cm−1 indicate that long-chain aliphatic compounds may not be present or beyond the detection limit of the technique.

FTIR spectrum for the interior corrosion of the Cauldrom Rim.

The presence of silicates in the interior corrosion of the Cauldron Rim was confirmed by XRD with the identification of quartz (Supplementary Fig. S1) in the sample. Quartz (SiO2) is a crystalline mineral present in UK soils as sand grains40. Whilst the hardness of this sample can be explained by the presence of quartz crystals, no evidence for its blue/greenish colour such as copper(II) minerals was found. The exterior corrosion sample from the Cauldron Rim did not yield a diffractogram.

The Total Ion Chromatograms obtained from the analysis of the corrosion from the interior and exterior cauldron rim (Fig. 3) were very similar. Both contain peaks identified as medium-chain n-alkenes [3, 4 and 5], two ubiquitous long-chain carboxylic acids [7 and 8] and long-chain aliphatic compounds. Most compound measurements, represented by unique m/z values, were detected in the exterior corrosion sample, which included a relatively high abundance peak matched to a plant metabolite aromatic hydrocarbon [1].

Total Ion Chromatograms obtained from the solid Cauldron Rim corrosion samples Compounds identified [1] Cymene; [2] Dodecene; [3] Tridecene; [4] Tetradecene; [5] Pentadecene; [6] Undecyl-benzene; [7] n-Hexadecanoic acid; [8] Octadecanoic acid and [*] long-chain aliphatic compounds. Spectral information is included in Supplementary Tables S1, 2.

The FTIR spectra of Vessel A corrosion samples (Supplementary Fig. S1) yielded only broad peaks that could not be assigned to any chemical function. By contrast, four mineral phases were identified in these samples by XRD (Fig. 4). The interior sample was characterized as 75% Pb3(CO3)2(OH)2 (hydrocerussite) and 25% Pb10(CO3)6O(OH)6 (plumbonacrite). The presence of these compounds in the sample may reflect the composition of the alloy used to make the vessel41 where lead corroded preferentially to copper42. Alternatively, the lead carbonates may relate to vessel use, given that in Roman times lead carbonate was used as make-up and added to medicinal preparations for the treatment of ulcers43,44.

Diffractograms obtained by XRD for the Vessel A corrosion with phase identification plumbonacrite and hydrocerusside identified in the interior sample, chalcocite and silicon oxide (quartz) identified in the exterior sample.

The exterior corrosion of Vessel A was characterized as 86% quartz and 14% Cu2S (chalcocite). Cuprous sulfides (including chalcocite) are typically dark corrosion products found on archaeological copper alloy objects45 that have been exposed to sulfate-reducing bacteria in anaerobic conditions46.

The organic compounds recovered from these samples were also intriguing. The Total Ion Chromatograms obtained from the corrosion of Vessel A (Fig. 5) were dominated by two peaks identified as long-chain carboxylic acids [12 and 15]. However, polycyclic aromatic hydrocarbons [3, 5, 8, 9, 13, 16], phthalate [4] and long-chain aliphatic nitriles [10 and 14] were only identified in the exterior sample.

Total Ion Chromatograms obtained from the solid Vessel A corrosion samples.

Compounds identified: [1] 5-methyl Furfural/benzaldehyde; [2] Methenamine; [3] 1-methyl Naphthalene; [4] Phthalate; [5] 2,6-Diisopropylnaphthalene; [6] Pentadecanal; [7] Tetradecanoic acid; [8] Fluorenone; [9] Phenanthrene; [10] aliphatic compound containing nitrile functional group; [11] Hexadecanoid acid methyl ester; [12] n-Hexadecanoic acid; [13] 2-phenyl Naphthalene; [14] 9-Octadecenitrile; [15] Octadecanoic acid; [16] Pyrene; [17] Octadecanoic acid, butyl ester. Spectral information is listed in Supplementary Tables S3, 4.

The origin of PAHs in the environment is often attributed to anthropogenic action (i.e. burning of wood47 and fossil fuels such as bitumen)48,49. Copper alloy vessels are reported to have been coated in bituminous substances to protect them from fire damage but their markers (i.e. a homologous n-alkanes series, hopanes, steranes and terpanes patterns)50,51,52 were either not present in the sample or are not detectable by the method used in this study. Additional analysis of the exterior corrosion sample targeting bitumen markers53 would be required to provide conclusive evidence of the absence of these markers.

PAHs can also have a biological source. These compounds have been detected in the tropical forest54, sediments55, soils56, in peatlands flora57, in Magnolia flowers58, termite nests59 (as a microbial metabolite and as a decomposition product of plant material) and as a fungus metabolite60. If we assume that the area between Vessel A and the cauldron originally contained plant remains as packing material (similar to the plant remains found under the scale plans in Vessel B), rainwater percolating through the soil would accumulate in this area facilitating its bacterial decay under an anaerobic environment. Such conditions could have led to the formation of PAHs61 and supported sulfate-reducing bacteria responsible for the chalcocite layer.

Analysis of the soil under Vessel B yielded a chromatogram (Fig. S3) dominated by hexadecanoic acid, an adipic acid ester, other minor compounds (including naphthalene), siloxanes but no compounds with the nitrile function. Long-chain alkyl nitriles are amongst the characteristic nitrogen-containing compounds of silty and clay soils62, occurring in nature as bacterial metabolites63, and detected as a pyrolytic product of archaeological soils rich in organic matter64. Thus the long-chain alkyl nitriles found in the exterior corrosion of Vessel A may indicate that this area of the hoard was once rich in organic matter.

The FTIR spectra of the corrosion samples from the interior of Vessel B (Supplementary Fig. S3) have only broad non-diagnostic peaks. In spite of their greenish/brown colour, the only crystalline phase identified in these samples was quartz, although many peaks remained unassigned, especially for the sample from the base of the vessel.

The Total Ion Chromatograms obtained from these samples were practically identical (Fig. 6). The compounds with the highest relative abundance peaks were identified as long-chain carboxylic acids [compounds 1–3 and 5], a compound normally associated with plasticizers [6], a triterpene [7], an animal sterol [10] and compounds containing a steroid nucleus [8 and 9].

Total Ion Chromatograms obtained from the solid Vessel B corrosion samples Compounds identified: [1] Tetradecanoic acid; [2] Pentadecanoic acid; [3] n-Hexadecanoic acid; [4] aliphatic compound containing a nitrile functional group; [5] Octadecanoic acid; [6] Phthalate [7] Squalene; [8] compound containing a steroid nucleus; [9] Cholesta-3,5-diene; [10] Cholesterol. Spectral information is listed in Supplementary Table S3.

The interior of Vessel B was the most protected area of the hoard, thus explaining the preservation of various plants remains. The most informative organic residue profile was obtained from the base/bottom sample of this vessel where squalene, cholesterol and its oxidation products were also identified.

Cholesterol is rarely found in organic residues extracted for archaeological ceramics65, possibly due to its degradation resulting from interactions with the fired clay and fatty acids, conditions created by cooking in clay pots66. Therefore, when cholesterol is identified in archaeological residues its source is considered to be modern contamination from fingerprints67, particularly when squalene is also present. However, cholesterol and its oxidation products have been identified in carbonized residues found in copper cauldrons20 , where the presence of copper ions has been suggested to have contributed to their preservation. It is also relevant that only cholesterol (not its oxidation products) was identified in modern freeze-dried milk and copper-milk corrosion33 analysed by the same GC-QTOF-MS with TSP method used in this study, and no sterols have been identified in any other sampls from the Pewsey Hoard.

The adoption of a multi-analytical protocol for the characterization of the Pewsey Hoard corrosion enabled us to identify organic and inorganic phases. The initial assumption regarding analytical techniques was that that FTIR and powder XRD could be used as screening techniques for organic and inorganic phases respectively. FTIR spectra were non-diagnostic even after suspension of the samples in KBr. Analysis by powder XRD was also challenging because some samples were not sufficiently large to yield a diffractogram or did not contain crystalline phases other than quartz.

The main technique for targeting organic residues was GC-QTOF-MS using a thermal separation probe. The technique supports an untargeted approach to sample characterization with practically no sample preparation. The wide range of compounds identified in the corrosion of the Pewsey Hoard vessels appear to reflect microclimates reflecting how the hoard was assembled and included biomarkers for animal fat found in the most protected area of the hoard from contact with the deposition environment.

Contamination is a major factor that complicates organic residue analysis in archaeology. In the case of corrosion samples, potential sources of contaminants include the deposition environment (e.g. soil, water), handling of the object during and post-excavation, contact with packaging, conservation treatments applied to the object in the field and contamination introduced during processing of samples in the laboratory. The Pewsey Hoard was excavated and transported to a museum by the finders, who probably did not wear gloves. Although precautions against contamination (wearing disposable gloves, using disposable metal scalpels and sterilized glass vials) were taken when sampling the vessels, it is possible that the sampled surfaces had already been contaminated prior to the arrival of the objects at the museum. It is tempting to disregard the findings presented in this study because of potential contamination and the absence of controls. However we hope that our study will raise awareness of the potential of metal corrosion products for organic residue analysis, a material that is often removed and discarded or considered a simple mixture of inorganic compounds.

Samples were analysed in reflection or in transmission mode. In reflection mode, the technique used was Attenuated Total Reflectance (ATR) where around 1 mg of sample was pressed against the reflective crystal of the equipment. In transmission mode, the technique used was the KBr pellet method. The sample was mixed with KBr in a 2/200 mg ratio. The mixture was pressed to form a 1 mm thick disc for analysis. Measurements were taken with an Excalibur Series Varian UMA600 as a combination of 64 scans between the 4000–400 cm−1 range and included background subtraction. Data was processed with Digilab Resolutions Pro 4.0 software, figures created with Spectragryph v.1.2.12 and band assignments were based on FTIR tables39,68.

The pulverized samples were set on a single crystal silicon plate using a PANalytical X’Pert PRO Cu alpha instrument at the Crystallography Laboratory in the Department of Chemistry, University of Oxford. The equipment was set to operate in continuous mode at 40 kV/40 mA with a scanned area set between 1° and 70° 2θ, 0.02 step size and 3° per minute. Data was processed using QualX© software with phase identification using the Crystallography Open Database (COD).

A glass microvial containing 3 mg of sample was placed inside the TSP attached to an Agilent 7890B gas chromatograph equipped with a Restek Rxi-5 ms column (30 m × 320 μm × 0.25 μm). The mass spectrometer was an Agilent 7250 GC/Q‑TOF equipped with a low-energy-capable EI source (70 eV). The TSP was set at 300 °C and the oven temperature set at 40 °C for one minute, increasing by 20 °C/minute until 320 °C where it was held for five minutes. Helium was used as a carrier gas, at 1.43L/min flow rate and 8.7psi pressure. The equilibration time was 0.5 min and the sample injection was splitless. The mass range was 50 to 650 m/z. All samples were run in triplicate with blanks added between samples. Data analysis was performed using Agilent Mass Hunter Qualitative Analysis 10.0 with compound assignments using NIST Library 17. Only compounds with a match factor (MF) and reverse match factor (RMF) > 700 and where the molecular ion is present with an accuracy mass error below 50 ppm were shortlisted.

The raw datasets used during the current study are available from the corresponding author on reasonable request.

Pires, E., Carvalho, L. C., Shimada, I. & McCullagh, J. Human blood and bird egg proteins identified in red paint covering a 1000-year-old gold mask from Peru. J. Proteome Res. 20, 5212–5217 (2021).

Article CAS Google Scholar

Lucas, A. Preservative Materials used by the Ancient Egyptians in Embalming (Nat. Printing Dep., 1911).

Evans, J. Come back king Alfred, All is Forgiven! In Organic Contents of Ancient Vessels: Materials Analysis and Archaeological Investigation (eds Biers, W. R. & McGovern, P. E.) 7–9 (MASCA, 1990).

Google Scholar

Evershed, R. P., Heron, C. P., Charters, S. & Goad, L. J. Chemical analysis of organic residues in ancient pottery: Methodological guidelines and applications. In Organic Residues in Archaeology: Their Identification and Analysis (eds White, R. & Page, H.) 11–25 (Institute for Conservation, 1990).

Google Scholar

Evershed, R. P. Experimental approaches to the interpretation of absorbed organic residues in archaeological ceramics. World Archaeol. 40, 26–47 (2008).

Article Google Scholar

Condamin, J., Formenti, F., Metais, M. O., Michel, M. & Blond, P. The application of gas chromatography to the tracing of oil in ancient amphorae. Archaeometry 18, 195–201 (1976).

Article Google Scholar

Evershed, R. P. Biomolecular archaeology and lipids. World Archaeol. 25, 74–93 (1993).

Article CAS Google Scholar

Robinson, N., Evershed, R. P., Higgs, W. H., Jerman, K. & Eglinton, G. Proof of a pine wood origin for pitch from Tudor (Mary Rose) and Etruscan shipwrecks: Application of analytical organic chemistry in archaeology. Analyst 112, 367–644 (1987).

Article Google Scholar

Hurst, W. J., Martin, R. A., Tarka, S. M. & Hall, G. D. Authentication of cocoa in Maya vessels using high performance liquid chromatographic techniques. J. Chromatogr. A. 466, 279–290 (1989).

Article CAS Google Scholar

Heron, C., Nemcek, N., Bonfield, K. M., Dixon, D. & Ottaway, B. S. The chemistry of Neolithic beeswax. Naturwissenschaften 81, 266–269 (1994).

Article CAS ADS Google Scholar

Stacey, R. J., Heron, C. & Sutton, M. K. The chemistry, archaeology and ethnography of a native American insect resin. J. Calif. Gt. Basin Anthropol. 20, 53–71 (1998).

Google Scholar

Copley, M. S. et al. Direct chemical evidence for widespread dairying in prehistoric Britain. PNAS 100, 1524–1529 (2003).

Article CAS ADS Google Scholar

Craig, O. E. et al. Did the first farmers of central and eastern Europe produce dairy foods? Antiquity 79, 882–894 (2005).

Article Google Scholar

Stacey, R. The composition of some Roman medicines: Evidence for Pliny’s Punic wax? Anal. Bioanal. Chem. 401, 1749–1759 (2011).

Article CAS Google Scholar

Pollard, A. M., Pellegrini, M. & Lee-Thorp, J. A. Technical note: Some observations on the conversion of dental enamel δ18op values to δ18ow to determine human mobility. Am. J. Phys. Anthropol. 145, 499–504 (2011).

Article CAS Google Scholar

Dunne, J. et al. The beginnings of dairying as practised by pastoralists in ‘Green’ Saharan Africa in the 5th millennium BC. Doc. Praehist. 40, 118–130 (2013).

Article Google Scholar

Salque, M. et al. Earliest evidence for cheese making in the sixth millennium BC in northern Europe. Nature 493, 522–525 (2013).

Article CAS ADS Google Scholar

Fulcher, K., Stacey, R. & Spencer, N. Bitumen from the dead sea in early iron age Nubia. Sci. Rep. 10, 8309 (2020).

Article CAS ADS Google Scholar

Peška, J., Králík, M. & Selucká, A. Organic matter residuals and imprints in products of copper and copper alloy corrosion: A preliminary study: Early bronze age industry. Pamatky Archeol. 97, 5–46 (2006).

Google Scholar

Steele, V. J. “Analysis of partially carbonised residues from the Chiseldon Cauldrons by gas chromatography-mass spectrometry and gas chromatography-combustion-isotope ratio mass spectrometry. In A Celtic Feast: The Iron Age Cauldrons from Chiseldon, Wiltshire (eds Baldwin, A. et al.) 78–86 (The British Museum, 2017).

Google Scholar

Sibley, L. R. & Jakes, J. A. Textile fabric pseudomorphs, a fossilized form of textile evidence. Cloth. Text. Res. 1, 24–30 (1982).

Article Google Scholar

Janaway, R. C. Dust to dust: The preservation of textile materials in metal artefact corrosion products with reference to inhumation graves. Sci. Arch. 27, 29–34 (1985).

Google Scholar

Edwards, G. Guidelines for dealing with material from sites where organic remains have been preserved by metal corrosion products. In: Evidence Preserved in Corrosion Products: New Fields in Artifact Studies. Occasional Papers (eds Janaway, R. C. & Scott, B.) 3–7 (UK Institute for Conservation, 1989).

Google Scholar

Angiorama, C. I., Campeny, S. M. L. L. & Taboada, C. Exceptional cases of textile mineralization in archaeological metallic objects from Santiago del Estero’s lowlands (Argentina). J. Archaeol. Sci. Rep. 33, 102478 (2020).

Google Scholar

Gillard, R. D., Hardman, S. M. Chapter 14 - Investigation of Fiber Mineralization Using Fourier Transform Infrared Microscopy. In: Archaeological Chemistry 173–186 (ACS Symposium Series 625, ACS, 1996).

Chapter Google Scholar

Merriman, K. R., Ditchfield, P., Goodburn-Brown, D. & Pollard, A. M. Where bio- and geochemistry meet: Organic Residues in copper-corrosion products? In Interdisciplinarity between Humanities and Science: A fetschrift in honour of Prof Df Henk Kars (eds Kluiving, S. et al.) 177–183 (Sidestone, 2017).

Google Scholar

Curt, W. B., Hostetter, E. & Stewart, D. R. A bronze situla from tomb 128, Valle Trebba: Chemical evidence of Resinated Wine at Spina. Stud. Etruschi. 59, 211–225 (1994).

Google Scholar

McGovern, P. E. et al. A funerary feast fit for King Midas. Nature 402, 863–864 (1999).

Article CAS ADS Google Scholar

Solazzo, C. et al. Species identification by peptide mass fingerprinting (PMF) in fibre products preserved by association with copper-alloy artefacts. J. Archaeol. Sci. 49, 524–534 (2014).

Article CAS Google Scholar

Oras, E., Higham, T. F. G., Cramp, L. J. E. & Bull, I. D. Archaeological science and object biography: A Roman bronze lamp from Kavastu bog (Estonia). Antiquity 91, 124–138 (2017).

Article Google Scholar

Carvalho, L. Chapter 2 - Corroding Copper in the Laboratory. In: Beyond Copper Soaps: Characterization of Copper Corrosion Containing Organics 5–11 (Springer Briefs in Applied Sciences and Technology, Springer, 2022).

Chapter Google Scholar

Carvalho, L. Chapter 3 - Copper-organic complexes synthetized electrochemically. In: Beyond Copper Soaps: Characterization of Copper Corrosion Containing Organics 13–39 (Springer Briefs in Applied Sciences and Technology, Springer, 2022).

Chapter Google Scholar

Carvalho, L. Chapter 4: Characterization of “Cu-Milk corrosion”. In: Beyond Copper Soaps: Characterization of Copper Corrosion Containing Organics 41–48 (SpringerBriefs in Applied Sciences and Technology, Springer, 2022).

Chapter Google Scholar

https://finds.org.uk/database/artefacts/record/id/720549.

Henry, R., Grant, M. J., Pelling, R. & Roberts, D. The Pewsey vessel hoard, an initial assessment. Wilts. Archaeol. Nat. Hist. Mag. 110, 230–233 (2017).

Google Scholar

Henry, R., Roberts, D., Grant, M. J., Pelling, R. & Marshall, P. A contextual analysis of the late roman Pewsey and Wilcot vessel hoards, Wiltshire. Britannia 50, 149–184 (2019).

Article Google Scholar

https://finds.org.uk/database/hoards/record/id/3305.

https://www.agilent.com/cs/library/brochures/5990-8715EN%20Thermo%20Sep%20Probe.pdf.

Socrates, G. Infrared and Raman Characteristic Group Frequencies 3rd edn. (Wiley, 2001).

Google Scholar

Rawlins, B. G. et al. Silicon (Si). In The Advanced Soil Geochemical Atlas of England and Wales. 158–161 (BGS 2012).

Frenkel, A. I. & Korshin, G. V. EXAFS studies of the chemical state of lead and copper in corrosion products formed on the brass surface in potable water. J. Synchrotron Rad. 6, 653–655 (1999).

Article CAS Google Scholar

Scott, D. A. Copper and Bronze in Art: Corrosion, Colorants, Conservation (Getty Conservation Institute, 2002).

Google Scholar

Welcomme, E., Walter, P., van Elslande, E. & Tsoucaris, G. Investigation of white pigments used as make-up during the Greco-Roman period. Appl. Phys. A Mater. Sci. Process 83, 551–556 (2006).

Article CAS ADS Google Scholar

Ursin, F., Borelli, C. & Steger, F. Dermatology in ancient rome: Medical ingredients in Ovid’s “remedies for female faces”. J. Cosmet. Dermatol. 19, 1388–1394 (2020).

Article Google Scholar

Huttunen-Saarivirta, E., Rajala, P. & Carpén, L. Corrosion behaviour of copper under biotic and abiotic conditions in anoxic ground water: Electrochemical study. Electrochim. Acta 203, 350–365 (2016).

Article CAS Google Scholar

Duncan, S. J., Ganiaris, H. Some sulfide corrosion products on copper alloys and lead alloys from London waterfront sites. in Recent Advances in the Conservation and Analysis of Artifacts: Jubilee Conservation Conference Papers, J. Black, Ed. (London Univ. Summer Schools, 1987) pp. 109–118.

Zou, S. et al. Paleofire indicated by polycyclic aromatic hydrocarbons in soil of Jinluojia archaeological site, Hubei, China. J. Earth Sci. 21, 247–256 (2010).

Article CAS Google Scholar

Baek, S. et al. A review of atmospheric polycyclic aromatic hydrocarbons: Sources, fate and behavior. Wat. Air Soil Poll. 60, 279–300 (1991).

Article CAS ADS Google Scholar

Peters, K. E., Walters, C. C. & Moldowan, J. M. The Biomarker Guide: Volume 1: Biomarkers and Isotopes in the Environment and Human History 2nd edn. (Cambridge Uni Press, 2005).

Google Scholar

Connan, J., Nissenbaum, A. & Dessort, D. Molecular archaeology: Export of dead sea asphalts to Canaan and Egypt in the Chalcolithic—Early Bronze Age (4th–3rd millennium BC). Geochim. Cosmochim. Acta 56, 2743–2759. https://doi.org/10.1016/0016-7037(92)90357-O (1992).

Article CAS ADS Google Scholar

Boëda, E. et al. Bitumen as a hafting material on middle palaeolithic artifacts. Nature 380, 336–338. https://doi.org/10.1038/380336a0 (1996).

Article ADS Google Scholar

Killops, S. D. & Killops, V. J. Introduction to Organic Geochemistry 2nd edn, 224 (Blackwell Publishing, 2005).

Google Scholar

Connan, J. & Connan, J. Use and trade of bitumen in antiquity and prehistory: Molecular archaeology reveals secrets of past civilizations. Philos. Trans. R. Soc. B Biol. Sci. 354, 33–50. https://doi.org/10.1098/rstb.1999.0358 (1999).

Article CAS Google Scholar

Wilcke, W., Amelung, W., Martius, C., Garcia, M. V. B. & Zech, W. Biological sources of polycyclic aromatic hydrocarbons (PAHs) in the amazonian rain forest Z. Pflanzenernähr. Bodenk 163, 27–30. https://doi.org/10.1002/(SICI)1522-2624(200002)163:1%3c27::AID-JPLN27%3e3.0.CO (2000).

3.0.CO" data-track-action="article reference" href="https://doi.org/10.1002%2F%28SICI%291522-2624%28200002%29163%3A1%3C27%3A%3AAID-JPLN27%3E3.0.CO" aria-label="Article reference 54" data-doi="10.1002/(SICI)1522-2624(200002)163:13.0.CO">Article CAS Google Scholar

Sporstol, S. et al. Source identification of aromatic hydrocarbons in sediments using GC/MS. Environ. Sci. Technol. 17, 282–286 (1983).

Article CAS ADS Google Scholar

Shamrikova, E. et al. Polyarenes distribution in the soil-plant system of reindeer pastures in the polar urals. Agronomy 12, 372. https://doi.org/10.3390/agronomy12020372 (2022).

Article CAS Google Scholar

Yakovleva, E. V., Gabov, D. N., Vasilevich, R. S. & Goncharova, N. N. Participation of plants in the formation of polycyclic aromatic hydrocarbons in peatlands. Eurasian Soil Sci. 53, 317–329. https://doi.org/10.1134/S1064229320030102 (2020).

Article CAS ADS Google Scholar

Azuma, H., Toyota, M., Asakawa, Y. & Kawano, S. Naphthalene: A constituent of Magnolia flowers. Phytochemistry 42, 999–1004. https://doi.org/10.1016/0031-9422(96)00082-9 (1996).

Article Google Scholar

Chen, J., Henderson, G., Grimm, C. C., Lloyd, S. W. & Laine, R. A. Termites fumigate their nests with naphthalene. Nature 392, 558–559. https://doi.org/10.1038/33305 (1998).

Article CAS ADS Google Scholar

Daisy, B. H. et al. Naphthalene, an insect repellent, is produced by Muscodor vitigenus, a novel endophytic fungus. Microbiology 148, 3737–3741. https://doi.org/10.1099/00221287-148-11-3737 (2002).

Article CAS Google Scholar

Thiele, S. & Brümmer, G. W. Bioformation of polycyclic aromatic hydrocarbons in soil under oxygen deficient conditions. Soil Biol. Biochem. 34, 733–735 (2002).

Article CAS Google Scholar

Schulten, H. R., Sorge, C. & Schnitzer, M. Structural studies on soil nitrogen by Curie-point pyrolysis-gas chromatography/mass spectrometry with nitrogen-selective detection. Biol. Fertil. Soils 20(3), 174–184 (1995).

Article CAS Google Scholar

Montes Vidal, D. et al. Long-chain alkyl cyanides: Unprecedented volatile compounds released by pseudomonas and micromonospora bacteria. Angew. Chem. Int. Ed. Engl. 56(15), 4342–4346 (2017).

Article CAS Google Scholar

Collins, J. A., Carr, A. S., Schefuß, E., Boom, A. & Sealy, J. Investigation of organic matter and biomarkers from Diepkloof Rock Shelter, South Africa: Insights into Middle Stone Age site usage and palaeoclimate. J. Archaeol. Sci. 85, 51–65 (2017).

Article CAS Google Scholar

Whelton, H. L. et al. A call for caution in the analysis of lipids and other small biomolecules from archaeological contexts. J. Archaeol. Sci. 132, 105397 (2021).

Article CAS Google Scholar

Hammann, S., Cramp, L. J. E., Whittle, M. & Evershed, R. P. Cholesterol degradation in archaeological pottery mediated by fired clay and fatty acid pro-oxidants. Tetrahedron Lett. 59, 4401–4404 (2018).

Article CAS Google Scholar

Smith, K. R. & Thiboutot, D. M. Thematic review series: Skin Lipids—Sebaceous gland lipids: Friend or foe? J. Lipid Res. 49, 271–281 (2008).

Article CAS Google Scholar

Cross, A. D. & Alan Jones, R. An Introduction to Practical Infra-red Spectroscopy 3rd edn. (Butterworth, 1969).

Book Google Scholar

Download references

Dr James Wickes for analytical support for the GC-QTOF-MS analyses, Dr Colin Johnston for access to FT-IR, Dr Amber Thompson for granting access to XRD and Dr Kourosh Abrahimi for the fruitful discussions. The authors also thank the University of Reading for funding the publication of this manuscript.

School of Archaeology, University of Oxford, Oxford, UK

Luciana da Costa Carvalho & A. Mark Pollard

Department of Archaeology, University of Reading, Reading, UK

Richard Henry

Chemistry Research Laboratory, Department of Chemistry, University of Oxford, Oxford, UK

Luciana da Costa Carvalho & James S. O. McCullagh

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Conceptualization: L.C., R.H., A.M.P.; methodology and investigation: L.C.; supervision: J.M., A.M.P.; writing original draft: L.C.; review and editing: R.H., J.M., A.M.P.

Correspondence to Luciana da Costa Carvalho.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Carvalho, L.d.C., Henry, R., McCullagh, J.S.O. et al. Unlocking the organic residues preserved in the corrosion from the Pewsey Hoard vessels. Sci Rep 12, 21284 (2022). https://doi.org/10.1038/s41598-022-24400-5

Download citation

Received: 19 April 2022

Accepted: 15 November 2022

Published: 09 December 2022

DOI: https://doi.org/10.1038/s41598-022-24400-5

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.